Method for manufacturing a nonvolatile semiconductor memory device

ABSTRACT

A method for manufacturing a semiconductor memory device includes forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer is formed adjacent the diffusion region of the semiconductor substrate. The method further includes forming a gate oxide layer over the gate stacked region, forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region, forming a nitride layer over the first conductive layers the nitride layer having an opening at the isolation layer, forming an oxide region in the first conductive layer using the nitride layer as a mask, removing the nitride layer and the silicon oxide region, forming an interelectrode dielectric layer over the first conductive layer, forming a second conductive layer over the interelectrode dielectric layer, the second conductive layer over the diffusion portion, removing the interelectrode dielectric layer over the diffusion portion, removing the first conductive layer over the diffusion portion and forming diffusion layer in the silicon substrate of the diffusion portion.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a method for manufacturing a nonvolatile semiconductor memory device such as an EEPROM (Electrically Erasable Programmable Read Only Memory).

[0003] 2. Description of the Related Art

[0004] An EEPROM is conventionally used as a nonvolatile semiconductor memory. FIG. 19, FIG. 20(A) and (B) show a conventional memory cell of the EEPROM. FIG. 19 shows a top view, FIG. 20(A) shows a cross sectional view along I-I line of FIG. 19, and FIG. 20(B) shows a cross sectional view along II-II line of FIG. 19.

[0005] A memory cell of the nonvolatile semiconductor memory device has a stacked gate portion 200 as shown in FIG. 19 and FIG. 20(A). The memory cell has a diffusion portion 300, which is formed at a peripheral portion of the stacked gate portion 200, as shown in FIG. 19 and FIG. 20(B). A stacked gate is formed between isolation layers 102. The isolation layers 102 are formed over a p-type silicon substrate 100. The stacked gate portion 200 has a gate oxide layer 106, a first gate electrode (floating gate electrode) 108, an interelectrode dielectric layer 110, a second gate electrode (control gate electrode) 112, an intermediate insulating layer 114 and an interconnection 116. The gate oxide layer 106 is formed over the silicon substrate 100. The first gate electrode 108 is formed over the gate oxide layer 106. The interelectrode dielectric layer 110 is formed over the first gate electrode 108. The second gate electrode 112 is formed over the interelectrode dielectric layer 110. The intermediate insulating layer 114 is formed over the second gate electrode 112.

[0006] The diffusion portion 300 has the isolation layers 102, a diffusion layer 118, the gate oxide layer 106, the intermediate insulating layer 114 and a contact hole 120 as shown in FIG. 20(B). The diffusion layer 118 is formed in the silicon substrate 100. The gate oxide layer 106 is formed over the silicon substrate 100. The intermediate insulating layer 114 is formed over the isolation layers 102. An interconnecting metal is filled in the contact hole 120, and forms the interconnection 116.

[0007] FIGS. 21(A)-23(H) show a method for manufacturing the conventional EEPROM. FIG. 21(A)-(E,), FIG. 22(A)-(D) and FIG. 23(A)-(D) correspond to line I-I of FIG. 19. FIG. 21(F)-(J), FIG. 22(E)-(H) and FIG. 23(E)-(H) correspond to line II-II of FIG. 19.

[0008] The isolation layers 102 are formed over the silicon substrate 100. Active regions 200 x and 300 x are formed over the silicon substrate 100 in this process as shown in FIG. 21(A) and FIG. 21(F). The gate oxide layer 106 is formed over active regions 200 x and 300 x as shown in FIG. 21(B) and FIG. 21(G). A first polysilicon layer 108 x is formed over the isolation layer 102 and the gate oxide layer 106 as shown in FIG. 21(C) and FIG. 21(H). The first polysilicon layer 108 x is used as the first gate electrode 108.

[0009] A resist pattern 124 is formed over the first polysilicon layer 108 x as shown in FIG. 21(D) and FIG. 21(1). The resist pattern 124 has an opening over the isolation layer 102. An etching is performed using the resist pattern 124 as a mask. The first polysilicon layer 108 x is separated in this etching as designed by reference number 108 y shown in FIG. 21(E) and FIG. 21(J).

[0010] The interelectrode dielectric layer 110 x is formed over the silicon substrate 100 after the resist pattern 124 is removed as shown in FIG. 22(A) and FIG. 22(E). A second polysilicon layer 112 x is formed over the interelectrode dielectric layer 110 x and the gate oxide layer 106 as shown in FIG. 22(B) and FIG. 22(F).

[0011] A resist pattern 126 is formed over the stacked gate portion 200 as shown in FIG. 22(C) and FIG. 22(G). An etching is performed using the resist pattern 126 as a mask. The second polysilicon layer 112 x over the diffusion portion 300 is removed by this etching as shown in FIG. 22(H), and the second polysilicon layer 112 x formed over the stacked gate portion 200 remains as shown in FIG. 22(D). Then, etchings are performed using the resist pattern 126 as a mask. The interelectrode dielectric layer 110 x and the first polysilicon layer 108 y over the diffusion portion 300 are removed, as shown in FIG. 23(A), (B), (E) and (F).

[0012] The resist pattern 126 is removed, and an implantation of ions (for example As) is performed. Then, a thermal diffusion is performed. The diffusion layer 118 at the diffusion portion 300 x is formed by this process as shown in FIG. 23(C) and FIG. 23(G). A BPSG (Boron-Phosphate-Silicate-Glass) layer as the intermediate insulating layer 114 is formed over the silicon substrate 100. A resist pattern (not shown in FIG. 23) is formed over the intermediate insulating layer. The resist pattern has an opening over the diffusion layer 118. An etching is performed using the resist pattern as a mask. This etching forms the contact hole 120 as shown in FIG. 23(D) and FIG. 23(H). The contact hole 120 is filled a metal layer. The metal layer is also formed over the intermediate insulating layer 114. The metal layer is patterned according to a pattern of the interconnect 116.

[0013] However, in the conventional nonvolatile semiconductor memory device, a concave portion is formed in the isolation layer 102 of the diffusion portion 300 during the etching of the interelectrode dielectric layer 108. Therefore, ions are introduced under the isolation layer 102. This causes a formation of an unnecessary diffusion layer 128, and adjacent diffusion portions are connected each other.

SUMMARY OF THE INVENTION

[0014] A method for manufacturing a semiconductor memory device includes forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer is formed adjacent the diffusion region of the semiconductor substrate. The method further includes forming a gate oxide layer over the gate stacked region, forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region, forming a nitride layer over the first conductive layers the nitride layer having an opening at the isolation layer, forming an oxide region in the first conductive layer using the nitride layer as a mask, removing the nitride layer and the silicon oxide region, forming an interelectrode dielectric layer over the first conductive layer, forming a second conductive layer over the interelectrode dielectric layer, the second conductive layer over the diffusion portion, removing the interelectrode dielectric layer over the diffusion portion, removing the first conductive layer over the diffusion portion and forming diffusion layer in the silicon substrate of the diffusion portion.

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] FIGS. 1(A)-(B) show a nonvolatile semiconductor memory device of a first preferred embodiment. FIG. 1(A) shows a cross sectional view along an I-I line of FIG. 2. FIG. 1(B) shows a cross sectional view along an II-II line of FIG. 2.

[0016]FIG. 2 shows a top view of the nonvolatile semiconductor memory device of the first preferred embodiment.

[0017] FIGS. 3(A)˜(F) show a method for manufacturing the nonvolatile semiconductor memory device of the first preferred embodiment. FIGS. 3(A)˜(C) correspond to the FIG. 1(A). FIGS. 3(D)˜(F) correspond to the FIG. 1(B).

[0018] FIGS. 4(A)˜(F) show the method for manufacturing the nonvolatile semiconductor memory device of the first preferred embodiment. FIGS. 4(A)˜(C) correspond to the FIG. 1(A). FIGS. 4(D)˜(F) correspond to the FIG. 1(B).

[0019] FIGS. 5(A)˜(F) show the method for manufacturing the nonvolatile semiconductor memory device of the first preferred embodiment. FIGS. 5(A)˜(C) A correspond to the FIG. 1(A). FIGS. 5(D)˜(F) correspond to the FIG. 1(B).

[0020] FIGS. 6(A)˜(F) show the method for manufacturing the nonvolatile semiconductor memory device of a second preferred embodiment. FIGS. 6(A)˜(C) correspond to the FIG. 1(A). FIGS. 6(D)˜(F) correspond to the FIG. 1(B).

[0021] FIGS. 7(A)˜(H) show a method for manufacturing of a third preferred embodiment. FIGS. 7(A)˜(D) correspond to a stacked gate portion. FIGS. 7(E)˜(H) and correspond to a diffusion portion.

[0022] FIGS. 8(A)˜(F) show the method for manufacturing of the third preferred embodiment. FIGS. 8(A)˜(C) correspond to the stacked gate portion. FIGS. 8(D)˜(F) correspond to the diffusion portion.

[0023] FIGS. 9(A)˜(F) show a method for manufacturing of a fourth preferred embodiment. FIGS. 9(A)˜(C) correspond to the stacked gate portion. FIGS. 9(D)˜(F) correspond to the diffusion portion.

[0024] FIGS. 10(A)˜(D) show the method for manufacturing of the fourth preferred embodiment. FIGS. 10(A)˜(B) correspond to the stacked gate portion. FIGS. 10(C)˜(D) correspond to the diffusion portion.

[0025] FIGS. 11(A)˜(H) show a method for manufacturing of a fifth preferred embodiment. FIGS. 11(A)˜(D) correspond to the stacked gate portion. FIGS. 11(E)˜(H) correspond to the diffusion portion.

[0026] FIGS. 12(A)˜(H) show the method for manufacturing of the fifth preferred embodiment. FIGS. 12(A)˜(D) correspond to the stacked gate portion. FIGS. 12(E)˜(H) correspond to the diffusion portion.

[0027] FIGS. 13(A)˜(H) show a method for manufacturing of a sixth preferred embodiment. FIGS. 13(A)˜(D) correspond to the stacked gate portion. FIGS. 13(E)˜(H) correspond to the diffusion portion.

[0028] FIGS. 14(A)˜(H) show the method for manufacturing of the sixth preferred embodiment. FIGS. 14(A)˜(D) correspond to the stacked gate portion. FIGS. 14(E)˜(H) correspond to the diffusion portion.

[0029] FIGS. 15(A)˜(F) show the method for manufacturing of the sixth preferred embodiment. FIGS. 15(A)˜(C) correspond to the stacked gate portion. FIGS. 15(D)˜(F) correspond to the diffusion portion.

[0030] FIGS. 16(A)˜(F) show a method for manufacturing of a seventh preferred embodiment. FIGS. 16(A)˜(C) correspond to the stacked gate portion. FIGS. 16(D)˜(F) correspond to the diffusion portion.

[0031] FIGS. 17(A)˜(H) show a method for manufacturing of a eighth preferred embodiment. FIGS. 17(A)˜(D) correspond to the stacked gate portion. FIGS. 17(E)˜(H) correspond to the diffusion portion.

[0032] FIGS. 18(A)˜(H) show the method for manufacturing of the eighth preferred embodiment. FIGS. 18(A)˜(D) correspond to the stacked gate portion. FIGS. 18(E)˜(H) correspond to the diffusion portion.

[0033]FIG. 19 shows a conventional nonvolatile semiconductor memory device. FIG. 19 shows a top view of the conventional nonvolatile semiconductor memory device.

[0034] FIGS. 20(A)-(B) shows the conventional nonvolatile semiconductor memory device. FIG. 20(A) shows a cross sectional view along I-I line of FIG. 19, and FIG. 20(B) shows a cross sectional view along II-II line of FIG. 19.

[0035] FIGS. 21(A)-(E) show a method for manufacturing the conventional nonvolatile semiconductor memory. FIGS. 21(A)-(E) correspond to line I-I of FIG. 19. FIGS. 21(F)-(J) correspond to line II-II of FIG. 19.

[0036] FIGS. 22(A)-(H) show the method for manufacturing the conventional nonvolatile semiconductor memory. FIGS. 22(A)-(D) correspond to line I-I of FIG. 19. FIGS. 22(E)-(H) correspond to line II-II of FIG. 19.

[0037] FIGS. 23(A(-(H) show the method for manufacturing the conventional nonvolatile semiconductor memory. FIGS. 23(A)-(D) correspond to line I-I of FIG. 19. FIGS. 23(E)-(H) correspond to line II-II of FIG. 19.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0038] First embodiment

[0039]FIG. 1 shows a nonvolatile semiconductor memory device of a first embodiment. FIGS. 1(A) and 1(B) are cross sectional views of the nonvolatile semiconductor memory device of the first preferred embodiment. FIG. 2 shows a top view of the nonvolatile semiconductor memory device of the first preferred embodiment. FIG. 1(A) shows a cross sectional view along an X-X line of FIG. 2. FIG. 1(B) shows a cross sectional view along an Y-Y line of FIG. 2.

[0040] The semiconductor memory device has a p-type silicon substrate 10 (not shown in FIG. 2), an isolation layer 12, a stacked gate portion 16 and a diffusion portion 18 as shown in FIG. 2. The stacked gate portion 16 has a gate oxide layer 20, a first polysilicon gate 22 formed over the gate oxide layer 20, an interelectrode dielectric layer 24 formed over the first gate electrode 22 and a second gate oxide layer 24 formed over the interelectrode dielectric layer 24 as shown in FIG. 1(A). The intermediate insulating layer 32 is formed over the second gate electrode 26 and an interconnection 36 is formed over the intermediate insulating layer 32 as shown in FIG. 1(A). The diffusion portion 28 has an isolation layer 12, a diffusion layer 28, a gate oxide layer 20 formed over the diffusion layer 28, an intermediate insulating layer 32, a contact hole 34 and an interconnection 36. The intermediate insulating layer 32 is formed over the gate oxide layer 20 and the isolation layer 12. The contact hole 34 is formed in the intermediate insulating layer 32. An interconnecting metal is filled in the contact hole 34 and connected to the diffusion layer 28, and the interconnecting material also forms the interconnection 36. The first gate electrode of the semiconductor memory device has a tapered shape in side surfaces 22 a as shown in FIG. 1(A).

[0041] FIGS. 3(A)˜(C), FIGS. 4(A)˜(C) and FIGS. 5(A)˜(C) show a method for manufacturing the semiconductor memory device. FIGS. 3(A)˜(C), FIGS. 4(A)˜(C) and FIGS. 5(A)˜(C) correspond to the FIGS. 1(A). FIGS. 3(D)˜(F), FIGS. 4(D)˜(F) and FIGS. 5(D)˜(F) show a method for manufacturing the semiconductor memory device. FIGS. 3(D)˜(F), FIGS. 4(D)˜(F) and FIGS. 5(D)˜(F) correspond to the FIG. 1(B).

[0042] The isolation layer 12 is partly formed over the semiconductor substrate 10 using a LOCOS method, and this results in the formation of active regions at the stacked gate potion 16 x and the diffusion portion 18 x. The gate oxide layer 28 is formed over the active regions 16 x. The gate oxide layer 20 is formed using a thermal oxidation. The first polysilicon layer 22 x is formed over the isolation layer 12 and the gate oxide layer 20. The first polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 using a LP-CVD method as shown in FIG. 3(A) and FIG. 3 (D).

[0043] Then, a nitride layer 40 is formed over the first polysilicon layer 22 x. A resist pattern is formed on the nitride layer 40. A photolithography is performed, and the resist pattern is patterned to have openings corresponding to the isolation layers 12. The nitride layer 40 is etched using the resist pattern as a mask. The nitride layer 40 is patterned to have openings corresponding to the isolation layers 12 as shown in FIG. 3(B) and FIG. 3(E). Oxidation of the polysilicon layer 22 x is performed using the nitride layer 40 as a mask as shown in FIG. 3(C) and FIG. 3(F). A region of the first polysilicon layer 22 x, which correspond to the Is openings of the nitride layer 40, is oxidized. This region is called a silicon oxide region 44 herein after.

[0044] The nitride layer 42 and the silicon oxide region 44 are removed, and the first gate electrode 22 is formed. The first gate electrode 22 has a tapered shape on the side surfaces because thereof as a result of the thermal oxidation process.

[0045] Then, the interelectrode dielectric layer 24 x is formed over the whole surface of the silicon substrate 10. The interelectrode dielectric layer 24 x has three layers, that is, a first oxide layer, a nitride layer and a second oxide layer (ONO layer). The oxide layers are formed using a thermal oxidation, and the nitride layer is formed using a LP-CVD method as shown in FIGS. 4(A) and 4(D).

[0046] A second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIGS. 4(B) and 4(F). The second polysilicon layer 26 x is formed using an LP-CVD method. The second polysilicon layer 26 x over the diffusion portion 18 x is removed, and the second gate electrode 26 is formed. The removal of the second polysilicon layer 26 x is performed by using a photo lithography technique. Therefore, a resist pattern 46 is formed over the semiconductor substrate 10 as shown in FIG. 4(C) and 4(F). The resist pattern 46 is formed over the stacked gate portion 16 x, The resist pattern also covers the isolation layer 12 of the stacked gate portion 16 x, and is not formed over the diffusion region 18 x. The dry etching is performed using the resist pattern 46 as a mask. As shown in FIG. 5(A) and FIG. 5(D), the interelectrode dielectric layer 24 x and the first gate electrode 22 over the diffusion portion 18 x is sequentially removed using the resist pattern 46 as a mask.

[0047] N-type ions (As) are introduced to the diffusion portion 18 x, and are diffused to the diffusion portion 18 x. The diffusion layer 28 is formed at the diffusion portion 18 x as shown in FIG. 5(E). The diffusion is performed using a thermal diffusion.

[0048] The intermediate insulating layer 32 is formed over the semiconductor substrate 10. The intermediate insulating layer 32 is a BPSG layer in the first preferred embodiment. The BPSG layer 32 is formed using a thermal CVD method. A resist pattern is formed over the intermediate insulating layer 32, and the resist pattern has an opening over the diffusion portion 18 x. A dry etching is performed using the resist pattern as a mask, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 5(C) and FIG. 5(F). The metal layer for interconnection 36 is formed over the intermediate insulating layer 32, and the contact hole 34 is filled with the metal layer as shown in FIG. 1(A) and 1(B).

[0049] The nonvolatile semiconductor memory device of FIGS. 1(A)-1(B) and FIG. 2 is formed as described above.

[0050] In the first preferred embodiment, the side surface portions of the first gate electrode have a taper shape the silicon oxide region. Therefore, the period for removal of the interelectrode dielectric layer 24 x is shortened, and the isolation layer reduction of the isolation layer 12 is prevented.

[0051] The area of the interelectrode dielectric layer, which contacts to the gate electrodes, is wider than that of the conventional nonvolatile semiconductor memory because of the tapered shape of the side surface portions of the gate electrodes. Therefore, the thickness of the interelectrode dielectric layer 24 can be reduced, and an efficiency of the electron introduction to the first gate electrode can be increased.

[0052] Second preferred embodiment

[0053] A semiconductor memory device of a second preferred embodiment has a same structure as that of the first preferred embodiment. However, as described below, a method for manufacturing of the second preferred embodiment is different from that of the first preferred embodiment.

[0054] FIGS. 6(A)˜(F) show a method for manufacturing the semiconductor memory device. FIGS. 6(A)˜(C) correspond to the FIG. 1(A). FIGS. 6(D)˜(F) correspond to the FIG. 1(B).

[0055] The isolation layer 12 is partly formed over the semiconductor substrate 10, and active regions of the stacked gate potion 16 x and the diffusion portion 18 x are formed. The gate oxide layer is formed over the active region. The gate oxide layer 20 is formed using a thermal oxidation. The first polysilicon layer 22 x is formed over the isolation layer 12 and the gate oxide layer 20 as shown in FIG. 3(A) and FIG. 3 (D). The polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 by using an LP-CVD method.

[0056] A resist pattern 52 is formed over the first polysilicon layer 22 x as shown in FIG. 6(A) and FIG. 6(D) in the second preferred embodiment. The resist pattern 52 has an opening 50 over the isolation layer 12. A width of the opening is approximately the same as a width of the isolation layer 12.

[0057] A wet etching is performed using the resist pattern 52 as a mask. The wet etching is stopped when the surface of the isolation layer 12 is exposed. An etching of the wet etching is a mixed liquid of HNO₃ and HF. The wet etching is an isotropic etching, therefore side surfaces of the first polysilicon layer 22 x have a tapered shape as shown in FIG. 6(B) and FIG. 6(E). Then, the resist pattern 52 is removed.

[0058] An interelectrode dielectric layer 24 x is formed over the first gate electrode 22 y as shown in FIG. 6(C) and 6(F). The interelectrode dielectric layer 24 x of the second preferred embodiment is the same as that of the first preferred embodiment (ONO layer). The second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIG. 4(B) and 4(E), and etched in the same way of the first preferred embodiment. An etching of the interelectrode dielectric layer 24 x and the first gate electrode 22 y is the same as the first preferred embodiment. The resist pattern 46 is removed, and As ions are introduced to the semiconductor substrate 10. The n-type diffusion layer 28 is formed as shown in FIG. 5(B) and 5(E) after the thermal diffusion. The intermediate insulating layer 32 is formed over the semiconductor substrate 10, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 5(C) and 5(F). The interconnection 36 formed over the intermediate insulating layer 32.

[0059] In the second preferred embodiment, the side surface of the first gate electrode 22 has a taper shape as a result of the isotropic etching. Therefore, the time period for removal of the interelectrode dielectric layer 24 x is shortened, and reduction of the isolation layer 12 is prevented.

[0060] The area of the interelectrode dielectric layer, which contacts to the gate electrodes, is wider than in the conventional nonvolatile semiconductor memory in the second preferred embodiment. Therefore, the thickness of the interelectrode dielectric layer 24 can be reduced, and an efficiency of the electron introduction to the first gate electrode can be increased.

[0061] Third preferred embodiment

[0062] FIGS. 7(A)˜(H) and FIGS. 8(A)˜(F) show a method for manufacturing of the third preferred embodiment. FIGS. 7(A)˜(D) and FIGS. 8(A)˜(C) correspond to the stacked gate portion. FIGS. 7(E)˜(H) and FIGS. 8(D)˜(F) correspond to the diffusion portion. The difference from the other preferred embodiments is mainly described below.

[0063] The isolation layer 12 is partly formed over the semiconductor substrate 10, and active regions of the stacked gate potion 16 x and the diffusion portion 18 x are formed. The gate oxide layer 20 is formed over the active region. The gate oxide layer 12 is formed using a thermal oxidation. The first polysilicon layer 22 is formed over the isolation layer 12 and the gate oxide layer 20.

[0064] The first polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 using an LP-CVD method as shown in FIG. 3(A) and FIG. 3 (D). A resist pattern 52 is formed over the first polysilicon layer 22 x as shown in FIG. 6(A) and FIG. 6(D). The resist pattern 52 has an opening 50 over the isolation layer 12.

[0065] A dry etching is performed using the resist pattern 52 as a mask, and the first gate electrode is formed. An interelectrode dielectric layer 24 x is formed over the first gate electrode 22 y. The interelectrode dielectric layer 24 x is the same as that of other preferred embodiments (ONO layer). The second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIG. 7(A) and FIG. 7(D). The second polysilicon layer 26 x over the diffusion portion is 18 x removed, and the second polysilicon layer 26 x remains as shown FIG. 7(B) and FIG. 7(E).

[0066] In the third embodiment, the wet etching is performed to remove the interelectrode dielectric layer 24 x, then, a dry etching is performed to remove the first gate electrode 22. The oxide layers of the interelectrode dielectric layer (ONO) is removed by using a dilute HF as an etching. The nitride layer of the interelectrode dielectric layer (ONO) is removed by using a hot phosphoric acid. A mask employed for these etchings is the resist pattern 46, which is formed in the etching of the second polysilicon layer 26 x. The wet etching is an isotropic etching, therefore the time period of the removing process is shortened, and the interelectrode dielectric layer 24 x is removed easily (FIG. 7(C) and 7(G). A dry etching is performed to remove the first gate electrode (FIG. 7(D) and 7(H). The interelectrode dielectric layer 24 x is removed by wet etching. Therefore, isolation layer reduction is prevented.

[0067] The resist pattern 46 is removed, and As ions are introduced to the semiconductor substrate 10. The diffusion layer 28 is formed in the same way as the first and second preferred embodiments (FIGS. 8(A) and 8(D). The intermediate insulating layer 32 is formed over the semiconductor substrate 10, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 8(B) and 8(E). The interconnection 36 is formed over the intermediate insulating layer 32 as shown in FIGS. 8(C) and 8(F).

[0068] In the third preferred embodiment, the interelectrode dielectric layer 24 x is removed by wet etching. Therefore, the isolation layer reduction is prevented.

[0069] Fourth embodiment

[0070] FIGS. 9(A)˜(F) and FIGS. 10(A)˜(D) show a method for manufacturing of the fourth preferred embodiment. FIGS. 9(A)˜(C) and FIGS. 10(A)˜(B) correspond to the stacked gate portion. FIGS. 9(D)˜(F) and FIGS. 10(C)˜(D) correspond to the diffusion portion. The difference from the other preferred embodiments is mainly described below.

[0071] The isolation layer 12 is partly formed over the semiconductor substrate 10, and the active regions of the stacked gate potion 16 x and the diffusion portion 18 x are formed. The gate oxide layer 20 is formed over the active region. The gate oxide layer 12 is formed using a thermal oxidation. The first polysilicon layer 22 x is formed over the isolation layer 12 and the gate oxide layer 20.

[0072] The first polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 using an LP-CVD method as shown in FIG. 3(A) and FIG. 3 (D).

[0073] A resist pattern is formed over the first polysilicon layer 22 x. The resist pattern has an opening over the isolation layer 12. A dry etching is performed using the resist pattern as a mask, and the first gate electrode 22 is formed. An interelectrode dielectric layer 24 x is formed over the first gate electrode 22 y. The interelectrode dielectric layer 24 x is the same as other preferred embodiments (ONO layer). The second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIG. 7(A) and FIG. 7(D). The second polysilicon layer 26 x over the diffusion portion is 18 x removed, and the second polysilicon layer 26 x remains as shown FIG. 7(B) and FIG. 7(E).

[0074] An etching of the interelectrode dielectric layer 24 x and the first gate electrode is performed as shown in FIG. 9(A) and 9(D). Therefore, the first gate electrode 23 of the stacked gate portion is formed. This etching results in an isolation layer reduction as shown in FIG. 9(D). A portion of reduction is called a layer reduction portion 12 x hereinafter.

[0075] The resist pattern, which used in the above described dry etching, is removed, and another resist pattern 54 is formed over the silicon substrate 10 using a photo lithography technique. The resist pattern 54 covers the layer reduction portion 12 x as shown in FIG. 9(B) and FIG. 9(E).

[0076] The As ions are introduced from the upper side of the substrate 10. Then, the resist pattern 54 is removed. A thermal diffusion is performed, and the diffusion layer 28 is formed as shown in FIG. 9(C) and FIG. 9(F).

[0077] The intermediate insulating layer 32 is formed over the semiconductor substrate 10, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 10(A) and 10(C). The interconnection 36 is formed over the intermediate insulating layer 32 as shown in FIG. 10(B) and FIG. 10(D).

[0078] The resist pattern 54 is formed over the layer reduction portion 12 x while As ions are introduced. Therefore, diffusion under the isolation layer is prevented.

[0079] Fifth embodiment

[0080] FIGS. 11(A)˜(H) and FIGS. 12(A)˜(H) show a method for manufacturing the semiconductor memory device of the fifth preferred embodiment. FIGS. 11(A)˜(D) and FIGS. 12(A)˜(D) correspond to the stacked gate portion. FIGS. 11(E)˜(H) and FIGS. 12(E)˜(H) correspond to the diffusion portion. The difference between this embodiment and the other preferred embodiments is described below.

[0081] The formation of the isolation layer 12. the first polysilicon layer and the interelectrode dielectric layer is performed in the same way as in the other embodiments. Then, the second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIG. 11(A) and FIG. 11(E).

[0082] In the fifth preferred embodiment, a resist pattern 56 is formed over the second polysilicon layer 26 x. The resist pattern 56 covers the stacked gate portion 16 x and the isolation layer of the diffusion portion 18 x. That is to say, the resist pattern 56 has an opening corresponding to an active region of the diffusion portion 18 x as shown in FIG. 11(B) and FIG. 11(F).

[0083] An etching of the second polysilicon layer 26 x is performed using the resist pattern 56 as a mask. The second polysilicon layer 26 x remains over the stacked gate portion 16 and the isolation layer 12 as shown in FIG. 11(C) and FIG. 11(G).

[0084] An etching of the interelectrode dielectric layer and the first gate electrode is further performed using the resist pattern 56 as a mask. Therefore, the first gate electrode 22 is formed as shown in FIGS. 11(D), 11(H), 12(A) and 12(E).

[0085] The resist pattern, which used in the above described etching, is removed. Then, As ions are introduced from the upper side of the substrate 10. A thermal diffusion is performed, and the diffusion layer 28 is formed as shown in FIG. 12(B) and FIG. 12(F).

[0086] The intermediate insulating layer 32 is formed over the semiconductor substrate 10, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 12(C) and FIG. 12(G). The interconnection 36 is formed over the intermediate insulating layer 32 as shown in FIG. 12(D) and FIG. 12(H).

[0087] In the fifth embodiment, the interelectrode dielectric layer 24 r and the second polysilicon layer 26 r remain over the isolation layer 12 of the diffusion portion 16. Therefore, these layers protect the isolation layer 12 from the isolation layer reduction, while the etching of the interelectrode dielectric layer 24 x is performed. Thus, the isolation layer reduction is prevented. These layers also prevent the introduction of ions under the isolation layer 12 while As ions are introduced.

[0088] Sixth embodiment

[0089] FIGS. 13A)˜(H), FIGS. 14(A)˜(H) and FIGS. 15(A)˜(F) show a method for manufacturing of the sixth preferred embodiment. FIGS. 13A)˜(D), FIGS. 14(A)˜(D) and FIGS. 15(A)˜(C) correspond to the stacked gate portion. FIGS. 13E)˜(H), FIGS. 14(E)˜(H) and FIGS. 15(D)˜(F) correspond to the diffusion portion. The difference from the other preferred embodiments is mainly described below.

[0090] The isolation layer 12 is partly formed over the semiconductor substrate 10, and the stacked gate potion 16 x and the diffusion portion 18 x are formed. The gate oxide layer is formed over the active region. The gate oxide layer 12 is formed using a thermal oxidation. The first polysilicon layer 22 is formed over the isolation layer 12 and the gate oxide layer 20.

[0091] In the sixth embodiment, a resist pattern 60 is formed over the silicon substrate. The resist pattern 60 has an opening corresponding to the isolation layer 12 of the diffusion portion 18 x.

[0092] Then, p-type ions (for example B+) are introduced to the silicon substrate 10 under the isolation layer 12 as shown in FIG. 13(B) and FIG. 13(F). The resist pattern 60 is removed after the introduction of the ions

[0093] The first polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 using an LP-CVD method as shown in FIG. 13(C) and FIG. 13 (G). A resist pattern 66 is formed over the first polysilicon layer 22 x. The resist pattern 66 has an opening over the isolation layer 12. A dry etching is performed using the resist pattern 66 as a mask, and the first gate electrode 22 is formed as shown in FIG. 13(D) and FIG. 13 (H). An interelectrode dielectric layer 24 x is formed over the first gate electrode. The interelectrode dielectric is the same as those of the other preferred embodiments (ONO layer). The second polysilicon layer 26 x is formed over the interelectrode dielectric layer 24 x as shown in FIG. 14(A) and FIG. 14 (E). The second polysilicon layer 26 x over the diffusion portion is removed as shown in FIG. 14(B) and FIG. 14(F).

[0094] An etching of the interelectrode dielectric layer 24 x and the first gate electrode 22 is performed as shown in FIG. 14(C) and 14(G). This etching results in an isolation layer reduction as shown in FIG. 14(H).

[0095] The introduction of As ions and the thermal diffusion are the same as those of the other embodiments. (FIG. 15(A) and FIG. 15(D)

[0096] The intermediate insulating layer 32 is formed over the semiconductor substrate 10, and the contact hole 34 is formed in the intermediate insulating layer 32 as shown in FIG. 15(B) and 15(E). The interconnection 36 if formed over the intermediate insulating layer 32 as shown in FIG. 15(C) and FIG. 15(F).

[0097] In the sixth preferred embodiment, the p-type ions are introduced under the isolation layer 12 of the diffusion portion. Therefore, even if the n-type ions are introduced under the isolation layer 12 of the diffusion portion, a conductive type is not changed, and the unnecessary diffusion layer is not formed.

[0098] Seventh embodiment

[0099] FIGS. 16(A)˜(F) show a method for manufacturing the semiconductor memory device of the seventh preferred embodiment. FIGS. 16(A)˜(C) correspond to the stacked gate portion. FIGS. 16(D)˜(F) correspond to the diffusion portion. The difference between this embodiment and the other preferred embodiments is described below. In particular, the seventh embodiment differs from the sixth. preferred embodiment in the order of the process steps.

[0100] The isolation layer 12 is partly formed over the semiconductor substrate 10, and the stacked gate potion 16 x and the diffusion portion 18 x is formed.

[0101] In the seventh embodiment, a resist pattern 70 is formed over the silicon substrate 10. The resist pattern 70 has an opening corresponding to the isolation layer 12 of the diffusion portion 18 x. Then, p-type ions (for example B+) are introduced to the silicon substrate 10 under the isolation layer 12 as shown in FIG. 16(B) and FIG. 16(E). The resist pattern 70 is removed after the introduction of the ions.

[0102] The gate oxide layer is formed over the active region after the introduction of p-type ions. The gate oxide layer 12 is formed using a thermal oxidation. Subsequent steps are the same as those of the sixth preferred embodiment.

[0103] In the seventh embodiment, the gate oxide layer is formed over the active region after the introduction of p-type ions. Therefore, the resist pattern is not formed on the gate oxide layer, and the gate oxide is not degraded because of organic materials included in the resist pattern.

[0104] Eighth embodiment

[0105] FIGS. 17(A)˜(H) and FIGS. 18(A)˜(H) show a method for manufacturing of the eighth preferred embodiment. FIGS. 17(A)˜(D) and FIGS. 18(A)˜(D) correspond to the stacked gate portion. FIGS. 17(E)˜(H) and FIGS. 18(E)˜(H) correspond to the diffusion portion. The difference from the other preferred embodiments is mainly described below.

[0106] The steps before the formation of the first polysilicon layer 22 are the same as the first embodiments. Then, the first polysilicon layer 22 x is formed over the whole surface of the silicon substrate 10 by using an LP-CVD method.

[0107] A resist pattern 74 is formed over the first polysilicon layer 22 x. The resist pattern 74 has an opening over the isolation layer 12. A dry etching is performed using the resist pattern as a mask, and the first gate electrode 22 is formed 18 x. Then, p-type ions (for example B+) are introduced to the silicon substrate 10 under the isolation layer 12 as shown in FIG. 17(B) and FIG. 17(F). The resist pattern 74 is removed after the introduction of the ions. Subsequent steps are the same as those of the sixth preferred embodiment.

[0108] In the eighth embodiment, the introduction of p-type ions is performed after the etching of the first polysilicon layer. Therefore, the resist pattern used for etching is commonly used for the introduction of p-type ions, and the steps associated with forming a resist patterns can be decreased.

[0109] As described above, according to the embodiments of the present invention, the isolation layer is prevented from the isolation layer reduction because of the tapered side surface of the first gate electrode. The area of the side surface of the first gate electrode is increased and thus a higher capacitance ratio can be obtained. The isolation layer is prevented from the isolation layer reduction because of the formation of the resist pattern over the isolation layer. The unnecessary diffusion layer is not formed because of introduction of the opposite type ions before formation of the diffusion layer.

[0110] Although the preferred embodiment of the present invention has been described in detail, it should be noted understood that various changes, substitutions and alternations can be made therein without departing from spirit and scope of the inventions as defined by the appended claims. 

What is claimed is
 1. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a nitride layer over the first conductive layers the nitride layer having an opening at the isolation layer; forming an oxide region in the first conductive layer using the nitride layer as a mask; removing the nitride layer and the silicon oxide region; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion; removing the interelectrode dielectric layer over the diffusion portion; removing the first conductive layer over the diffusion portion; forming diffusion layer in the silicon substrate of the diffusion portion.
 2. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a resist pattern over the first conductive layer, the resist pattern having an opening at a portion corresponding to the isolation layer; etching the first conductive layer using the resist pattern as a mask, the etching being wet etching; removing the resist pattern; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion; removing the interelectrode dielectric layer over the diffusion portion; removing the first conductive layer over the diffusion portion; forming diffusion layer in the diffusion portion.
 3. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a resist pattern over the first conductive layer, the resist pattern having an opening at a portion corresponding to the isolation layer; etching the first conductive layer using the resist pattern as a mask; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion, removing the interelectrode dielectric layer over the diffusion portion using a wet etching; removing the first conductive layer over the diffusion portion; forming a diffusion layer in the diffusion portion.
 4. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a first resist pattern over the first conductive layer, the resist pattern having an opening at a portion corresponding to the isolation layer; etching the first conductive layer using the first resist pattern as a mask; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion, removing the interelectrode dielectric layer over the diffusion portion; removing the first conductive layer over the diffusion portion; forming a second resist pattern at a portion corresponding to the isolation layer of the diffusion portion; and introducing ions to the diffusion portion using the resist pattern as a mask.
 5. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a first resist pattern over the first conductive layer, the first resist pattern having an opening at a portion corresponding to the isolation layer; etching the first conductive layer using the first resist pattern as a mask; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; forming a second resist pattern at a portion corresponding to the stacked gate portion and isolation layer of the diffusion portion; removing the second conductive layer over the diffusion portion using the second resist pattern as a mask; removing the interelectrode dielectric layer using the second resist pattern as a mask; removing the first conductive layer over the diffusion portion; introducing ions to the diffusion portion.
 6. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a resist pattern over the semiconductor substrate, the resist pattern having an opening over the isolation layer of the diffusion portion; introducing a first conductive type ion using the resist pattern as a mask; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming an interelectrode dielectric layer over the first conductive layer; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion; removing the interelectrode dielectric layer over the diffusion portion; removing the first conductive layer over the diffusion portion; introducing a second conductive type ion to the diffusion portion.
 7. The method for manufacturing a semiconductor memory device as claimed in claim 6, wherein the forming a resist pattern over the semiconductor substrate is performed before forming the gate oxide layer.
 8. A method for manufacturing a semiconductor memory device comprising: forming an isolation layer over a semiconductor substrate having a stacked gate region and a diffusion region, the isolation layer formed adjacent the diffusion region of the semiconductor substrate; forming a gate oxide layer over the gate stacked region; forming a first conductive layer over the isolation layer, the gate oxide layer and the diffusion region; forming a resist pattern over the first conductive layer, the resist pattern having an opening over the isolation layer; etching the first conductive layer using the resist as a mask; introducing a first conductive type ion using the resist pattern as a mask; forming a second conductive layer over the interelectrode dielectric layer; removing the second conductive layer over the diffusion portion, removing the interelectrode dielectric layer over the diffusion portion; removing the first conductive layer over the diffusion portion; introducing a second conductive type ion to the diffusion portion. 